關(guān)于鋁板在染色時(shí)影響其質(zhì)量的因素有哪些呢?我們一起來(lái)了解一下;
What factors affect the quality of aluminum plate in dyeing? Let's have a look;
氧化膜對于鋁板的質(zhì)量有很大的影響。氧化膜就是指鋁板在生產(chǎn)的過(guò)程中的厚度、孔隙率、透明度等。鋁板中膜層的厚度保持在10um以上就可以了，孔隙率以及透明度，這樣就可以得到比較好的染色質(zhì)量。
The oxide film has a great influence on the quality of aluminum plate. Oxide film refers to the thickness, porosity and transparency of aluminum plate in the production process. The thickness of the film in the aluminum plate should be kept above 10um. The porosity and transparency of the film can make the dyeing quality better.
染色的溫度
Dyeing temperature
鋁板在染色的過(guò)程中分為冷染與熱染。使用冷染，所耗費的時(shí)間比較長(cháng)，在染色的過(guò)程中期色彩的均勻性比較好掌握。熱染使用時(shí)間比較短，但是在染色的過(guò)程中對于顏色的操控比較難。熱染的溫度通常在10-60℃。如果在染色的過(guò)程中，溫度過(guò)高，會(huì )減小染色的吸附性，并且容易導致鋁板表面發(fā)花。
Aluminum plate can be divided into cold dyeing and hot dyeing. It takes a long time to use cold dyeing, and the uniformity of color is easy to master in the middle of dyeing process. The use time of hot dyeing is relatively short, but it is difficult to control the color in the dyeing process. The temperature of hot dyeing is usually 10-60 ℃. If the temperature is too high in the process of dyeing, the adsorption of dyeing will be reduced, and the surface of aluminum plate will be easy to flower.

鋁板制件原料的影響
Influence of raw materials on aluminum plate parts
通常我們在生產(chǎn)的過(guò)程中高純鋁、鋁鎂、鋁錳合金經(jīng)過(guò)陽(yáng)極氧化以后，其中染色的功能是好的，可以染成各種各樣的顏色。對于含有硅或銅比較重的板材，在染色的過(guò)程中只能夠染成深色與黑色，比較單調的顏色。
Generally, after anodizing of high purity aluminum, aluminum magnesium and aluminum manganese alloy, the dyeing function is the best and can be dyed into various colors. For the heavy plate containing silicon or copper, only dark and black colors can be dyed in the dyeing process.
染色液濃度
Dye concentration
鋁板的濃度與染色之間存在一定的聯(lián)系，如果鋁板染成淡色，其中濃度可以降低一點(diǎn)，染成深色濃度可以高一點(diǎn)。
There is a certain relationship between the concentration of aluminum plate and dyeing. If the aluminum plate is dyed in light color, the concentration can be reduced a little, and the dark color can be higher.
通常所生產(chǎn)的鋁板材料所染比較淡的顏色其色彩為0.1-0.39g/L，染淡色彩為1g/L，染深色彩為3-5g/L，染稠密的色彩為10-15g/L，如果要求的染色濃度比較高就會(huì )造成顏色不均或者會(huì )出現浮色的現象，在清潔與關(guān)閉的過(guò)程匯總容易產(chǎn)生流色。
Generally, the light color of aluminum plate material is 0.1-0.39g/l, light color is 1g / L, deep color is 3-5g / L, and dense color is 10-15g / L. if the required dyeing concentration is relatively high, it will cause uneven color or floating color phenomenon, which is easy to produce color flow in the process of cleaning and closing.
為了加強其染色的吸附性能，這樣可以使用低濃度顏色進(jìn)行延伸染色，這樣可以使染料能夠比較均勻的滲透到氧化膜中，這樣可以使染色更加和諧與牢固。
In order to strengthen the adsorption property of the dye, low concentration color can be used for extended dyeing, which can make the dye more evenly penetrate into the oxide film, which can make the dyeing more harmonious and firm.