        鋁板生產(chǎn)廠(chǎng)家告訴你什么鋁板能折彎?

        來(lái)源:http://www.gytimber.com/ 發(fā)布時(shí)間:2020-11-26

        鋁板在生產(chǎn)過(guò)程中是平整為片狀進(jìn)行售賣(mài)的,但有些建筑企業(yè)在使用鋁板時(shí)會(huì )選擇把鋁板折彎,折彎后便于施工使用,一般來(lái)說(shuō)薄一點(diǎn)的鋁板折彎是沒(méi)有問(wèn)題的,但厚一點(diǎn)的就需要使用一些工具進(jìn)行處理。處理過(guò)程相對來(lái)說(shuō)也比較簡(jiǎn)單,那么有朋友可能會(huì )產(chǎn)生疑問(wèn),什么類(lèi)型的鋁板可以折彎,折彎的鋁板是否硬度不夠?對于這些問(wèn)題,鋁板批發(fā)廠(chǎng)家做出如下解答。
        In the production process, aluminum plates are flat and sold in flakes, but some construction enterprises will choose to bend aluminum plates when using aluminum plates. After bending, it is convenient for construction and use. Generally speaking, there is no problem in bending thin aluminum plates, but some professional tools are needed for thicker ones. The processing process is relatively simple, so a friend may have questions, what type of aluminum plate can be bent, whether the bending aluminum plate hardness is not enough? For these questions, the aluminum plate wholesale manufacturers make the following answers.
        鋁板批發(fā)廠(chǎng)家提到在正常情況下,o狀態(tài)的鋁板折彎一般沒(méi)有問(wèn)題,但由于該狀態(tài)的鋁板過(guò)于柔軟,所以很少用該狀態(tài)的鋁板折彎。 同時(shí),選鋁板時(shí)要注意純鋁板和合金鋁板的區別。 一般來(lái)說(shuō)純鋁的硬度不怎么高。 具體而言,純鋁的彎折使用1100、1050、1060等,建議用1100H26的。
        Aluminum plate wholesalers mentioned that under normal conditions, there is no problem with aluminum plate bending in o state, but aluminum plate in this state is rarely used for bending because the aluminum plate in this state is too soft. At the same time, attention should be paid to the difference between pure aluminum plate and alloy aluminum plate when selecting aluminum plate. Generally speaking, the hardness of pure aluminum is not very high. Specifically, 1100, 1050 and 1060 are used for pure aluminum bending, and 1100h26 is recommended.


        一些合金鋁板硬度相對來(lái)說(shuō)會(huì )比較好一點(diǎn),一般可以使用3003、3005、5052等半硬狀態(tài)的鋁板進(jìn)行彎折。 6061、2024、7075的硬度過(guò)高,特別是T6的狀態(tài)應該不會(huì )彎曲。 只要不加溫彎曲,好鋁板和壞鋁板的區別在于氧化性能、公差、表面效果、結晶精度及均勻穩定性等,它們彎折的程度一般是不一樣的,效果也不是很明顯。
        The hardness of some alloy aluminum plates is relatively better. Generally, 3003, 3005, 5052 and other semi-hard aluminum plates can be used for bending. The hardness of 6061, 2024 and 7075 is too high, especially for T6. As long as the bending is not heated, the difference between good aluminum plate and bad aluminum plate lies in oxidation performance, tolerance, surface effect, crystallization accuracy and uniform stability. The bending degree of them is generally different, and the effect is not very obvious.
        對于可以折彎的鋁板還分為不同的厚度,厚度不同折彎的能力也不同,一般來(lái)說(shuō),薄一點(diǎn)的鋁板折彎是沒(méi)有問(wèn)題的,但相對來(lái)說(shuō)厚度大一點(diǎn)的,用手掰比較困難的可以選擇一些鉗子進(jìn)行輔助掰彎,在厚一點(diǎn)的就需要一些大型工具進(jìn)行加工處理了。
        The aluminum plates that can be bent are also divided into different thicknesses, and the bending ability is different with different thicknesses. Generally speaking, there is no problem for the aluminum plates with thinner thickness, but for those with larger thickness and more difficult to break by hand, some pliers can be selected for auxiliary bending, and some large tools are needed for processing the thicker ones.
        以上就是鋁板生產(chǎn)廠(chǎng)家介紹的鋁板可以折彎的類(lèi)型,不同厚度,不同硬度的鋁板在折彎時(shí)需要操作的步驟也不同,因此要根據鋁板具體的情況進(jìn)行處理。綜合考量,在采取措施,這樣在使用工程中也會(huì )比較順利。
        The above is the type of aluminum plate that can be bent as described by the aluminum plate manufacturer. Different thickness and hardness of aluminum plate require different operation steps during bending, so it should be handled according to the specific situation of aluminum plate. Comprehensive consideration, in the adoption of measures, this will be more smooth in the use of the project.